EAA食品级包装复合 乙烯甲基丙烯酸共聚物 EAA复合薄膜中的热封层或是粘结剂层

EAA与多种填充物、颜料、染料等有很好的相容性，但与胺、环氧化物以及金属的氢氧化物、氧化物、碳酸盐等共混或共挤时，若这些材料发生分解，将导致聚合物的交联和其他问题。

产品说明
PRIMACOR 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack
and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This
resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR).
 Excellent draw down and edge stability
 Excellent product resistance
 Excellent hot tack, heat seal, toughness
 High performance sealant or tie layer
Complies with:
 U.S. FDA 21 CFR 177.1310(b)
EU, No 10/2011
Consult the regulations for complete details.

总体
材料状态 已商用：当前有效
供货地区  亚太地区
机构评级  EU No 10/2011 FDA 21 CFR 177.1310 (b)
形式  颗粒料
物理性能 额定值 单位制 测试方法
比重 0.938 g/cm ASTM D792
ISO 1183
熔流率 2 (190°C/2.16 kg) 8.5 g/10 min ASTM D1238
ISO 1133
共聚单体含量 3 9.7 %
机械性能 额定值 单位制 测试方法
抗张强度 ASTM D638
ISO 527-2
屈服, 模压成型 7.93 MPa
断裂, 模压成型 17.6 MPa
伸长率 (断裂, 模压成型) 600 % ASTM D638
ISO 527-2
热性能 额定值 单位制 测试方法
维卡软化温度 81.1 °C ASTM D1525
ISO 306
溶融温度（DSC） 98.0 °C Internal Method
挤出 额定值 单位制 测试方法
熔体温度 260 到 290 °C
内缩量 (288°C, 25.4 m) 50.8 mm Internal Method
小涂层厚度 10 m Internal Method
小涂层重量 9.8 g/m Internal Method

EAA的透明性和韧性，降低了熔点和软化点。当MI相同时，随着AA含量的增加，EAA的透明性、韧性、粘接性、耐环境应力开裂性会增加；相反，其刚性、湿蒸汽透射率、抗蠕变性、耐化学性会更好。当AA含量相同时，随着MI的增加，EAA的粘接性、加工性会更好；相反，其韧性、耐环境应力开裂性会增加。